Quality bolts, nuts, screws, sockets and studs manufactured of quality materials to inch fastener standards Home of Vegas Fastener Manufacturing Vegas Fastener Manufacturing as a quality alloy, a blend of the skills, capabilities and extensive experience of its manufacturing team. What products we make and how we can manufacture what you need to your exact specifications Request a quote Contact Us

Toll Free: 888-651-9223            

Waspaloy Material Property Data Sheet

Do you need custom fasteners created with Waspaloy? Since our inception, Vegas Fastener Manufacturing has met every challenge of providing Quality, Timely, Cost-effective solutions for specialty fastener applications. Every product is built to your specifications, using your prints if necessary.

Below are the technical specifications of the Waspaloy Bar Stock we have available to meet your needs.

 

Waspaloy® Nickel Superalloy, Heat Treatment: 1010°C (1850°F) + Age


Subcategory: Metal; Nickel Base; Superalloy

Key Words: Allvac, an Allegheny Teledyne Company, UNS N07001; AMS 5704, 5706, 5707, 5708. ASTM B 637

Component   Wt. %
Al1.4 
B0.01 
C0.05 
Co13 
Component   Wt. %
Cr19.5 
Fe1 
Mo4.3 
Component   Wt. %
Ni57 
Ti3 
Zr0.7 

Material Notes:
Nickel content calculated as remainder. Data provided by Allvac.

Applications: Turbine compressor blades and discs, shafts, spacers, fasteners, miscellaneous jet engine hardware; space shuttle turbo pump seals.

Waspaloy is a registered trademark of Pratt & Whitney Aircraft.

Physical PropertiesMetricEnglishComments
Density8.19 g/cc0.296 lb/in³ 

Mechanical Properties
Hardness, Brinell351351 Estimated from Rockwell C value for Brinell test with 3000 kg load/10 mm diameter ball
Hardness, Knoop382382 Estimated from Rockwell C value.
Hardness, Rockwell C3838 
Hardness, Vickers367367 Estimated from Rockwell C value.
Tensile Strength, Ultimate1276 MPa185000 psi 
Tensile Strength, Yield897 MPa130000 psi 0.2% Offset
Elongation at Break23 %23 % 
Reduction of Area25 %25 % 

 


 This information is provided by MatWeb.com, The Online Materials Database and is reprinted with their permission.

Copyright 1996-2005 by Automation Creations, Inc.  The contents, results, and technical data on this page may not be reproduced either electronically, photographically or substantively without permission from Automation Creations, Inc and MatWeb.com. No warranty, neither expressed nor implied, is given regarding the accuracy of this information. The user assumes all risk and liability in connection with the use of information from MatWeb.com.