Inconel™ 925 Material Property Data Sheet
Do you need custom fasteners created with Inconel™ 925? Since our inception, Vegas Fastener Manufacturing has met every challenge of providing
Quality, Timely, Cost-effective solutions for specialty fastener applications. Every product is built to your specifications, using your prints if necessary.
Below are the technical specifications of the Inconel™ 925 Bar Stock we have available to meet your needs.
Special Metals INCOLOY® Alloy 925
Subcategory: Metal; Nickel Base; Superalloy
Key Words: UNS N09925; NACE MR-01-75
|Component|| Wt. %|
A precipitation-hardenable nickel-iron-chromium alloy with additions of molybdenum and copper. It combines the high strength of a precipitation-hardenable alloy with the excellent corrosion resistance of INCOLOY alloy 825. The alloy has outstanding resistance to general corrosion, pitting, crevice corrosion, and stress-corrosion cracking in many aqueous environments including those containing sulfides and chlorides. Used for surface and down-hole hardware in sour gas wells and for oil-production equipment. Standard product forms are round, flats, forging stock, pipe, tube, and wire.
Data provided by the manufacturer, Special Metals.
|Density||8.05 g/cc||0.291 lb/inł|| |
|Tensile Strength, Ultimate||1210 MPa||175000 psi|| Precipitation Hardened. Value at room temperature. Value at 550°C is 970 MPa.|
|Tensile Strength, Yield||810 MPa||117000 psi|| Precipitation Hardened. Value at room temperature; 0.2% offset. Value at 550°C is 700 MPa.|
|Elongation at Break||24 %||24 %|| Precipitation Hardened. Value at room temperature. Value at 550°C is 25%.|
|Electrical Resistivity||0.000117 ohm-cm||0.000117 ohm-cm|| |
|Magnetic Permeability||1.001||1.001|| at 200 oersted (15.9 kA/m)|
|CTE, linear 20°C||13.2 µm/m-°C||7.33 µin/in-°F|| 20-100°C|
|Heat Capacity||0.435 J/g-°C||0.104 BTU/lb-°F|| |
|Melting Point||1311 - 1366 °C||2390 - 2490 °F|| |
|Solidus||1311 °C||2390 °F|| |
|Liquidus||1366 °C||2490 °F|| ||
This information is provided by
MatWeb.com, The Online Materials Database and is reprinted with their permission.
Copyright 1996-2005 by Automation Creations, Inc.
The contents, results, and technical data on this page may not
be reproduced either electronically, photographically or substantively without permission from
Automation Creations, Inc and MatWeb.com. No warranty, neither expressed nor implied, is given
regarding the accuracy of this information. The user assumes all risk and liability in connection with the use of
information from MatWeb.com.