Quality bolts, nuts, screws, sockets and studs manufactured of quality materials to inch fastener standards Home of Vegas Fastener Manufacturing Vegas Fastener Manufacturing as a quality alloy, a blend of the skills, capabilities and extensive experience of its manufacturing team. What products we make and how we can manufacture what you need to your exact specifications Request a quote Contact Us

Toll Free: 888-651-9223            

Haynes HR-160 Material Property Data Sheet

Do you need custom fasteners created with Haynes HR-160? Since our inception, Vegas Fastener Manufacturing has met every challenge of providing Quality, Timely, Cost-effective solutions for specialty fastener applications. Every product is built to your specifications, using your prints if necessary.

Below are the technical specifications of the Haynes HR-160 Bar Stock we have available to meet your needs.


Haynes HR-160 alloy, annealed plate

Subcategory: Metal; Nickel Base; Superalloy

Key Words: UNS N12160, ASTM B435, ASTM B366, DIN No.2.4880

Component   Wt. %
FeMax 3.5 
Component   Wt. %
MoMax 1 
NbMax 1 
Component   Wt. %
WMax 1 

Material Notes:
Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmosperes. Excellent forming and welding characteristics. Applications include a variety of fabricated components in municipal, industrial, hazardous, and nuclear waste heat recovery systems. Also suitable for utility boilers, sulfur plants, high-temperature furnaces, kilns, calciners, resource recovery units, cement kilns, pulp and paper recovery boilers, coal gasification systems, and fluidized-bed-combustion systems.

Data provided by the manufacturer, Haynes International, Inc.

Physical PropertiesMetricEnglishComments
Density8.08 g/cc0.292 lb/in at RT

Mechanical Properties
Tensile Strength, Ultimate774 MPa112000 psi 
Tensile Strength, Yield321 MPa46600 psi at 0.2% offset
Elongation at Break66 %66 % in 50.8 mm
Reduction of Area73 %73 % 
Modulus of Elasticity211 GPa30600 ksi RT
Modulus of Elasticity at Elevated Temperature137 GPa19900 ksi 980C
Modulus of Elasticity at Elevated Temperature145 GPa21000 ksi 925C
Modulus of Elasticity at Elevated Temperature150 GPa21800 ksi 870C
Modulus of Elasticity at Elevated Temperature154 GPa22300 ksi 815C
Modulus of Elasticity at Elevated Temperature158 GPa22900 ksi 760C
Modulus of Elasticity at Elevated Temperature163 GPa23600 ksi 705C
Modulus of Elasticity at Elevated Temperature168 GPa24400 ksi 650C
Modulus of Elasticity at Elevated Temperature173 GPa25100 ksi 595C
Modulus of Elasticity at Elevated Temperature177 GPa25700 ksi 540C
Modulus of Elasticity at Elevated Temperature180 GPa26100 ksi 480C
Modulus of Elasticity at Elevated Temperature183 GPa26500 ksi 425C
Modulus of Elasticity at Elevated Temperature187 GPa27100 ksi 370C
Modulus of Elasticity at Elevated Temperature192 GPa27800 ksi 315C
Modulus of Elasticity at Elevated Temperature197 GPa28600 ksi 260C
Modulus of Elasticity at Elevated Temperature201 GPa29200 ksi 205C
Modulus of Elasticity at Elevated Temperature204 GPa29600 ksi 150C
Modulus of Elasticity at Elevated Temperature208 GPa30200 ksi 90C
Modulus of Elasticity at Elevated Temperature210 GPa30500 ksi 40C
Charpy Impact358 J264 ft-lb annealed, 58 J aged 1000 hours at 650C (1200F), 46 J aged 4000 hours at 650C (1200F), 42 J aged 8000 hours at 650C (1200F), 37 J aged 1000 hours at 760C (1400F), 24 J aged 4000 hours at 760C (1400F), 20 J aged 8000 hours at 760C (1400F), 22 J

Electrical Properties
Electrical Resistivity0.0001112 ohm-cm0.0001112 ohm-cm RT
Electrical Resistivity at Elevated Temperature0.0001231 ohm-cm0.0001231 ohm-cm 700C (1290F)
Electrical Resistivity at Elevated Temperature0.0001238 ohm-cm0.0001238 ohm-cm 800C (1470F)
Electrical Resistivity at Elevated Temperature0.0001245 ohm-cm0.0001245 ohm-cm 900C (1650F)
Electrical Resistivity at Elevated Temperature0.0001252 ohm-cm0.0001252 ohm-cm 1000C (1830F)
Electrical Resistivity at Elevated Temperature0.0001259 ohm-cm0.0001259 ohm-cm 1100C (2010F)
Electrical Resistivity at Elevated Temperature0.0001267 ohm-cm0.0001267 ohm-cm 1200C (2190F)

Thermal Properties
CTE, linear 20C13 m/m-C7.22 in/in-F 25-95C (77-200F)
CTE, linear 250C13.7 m/m-C7.61 in/in-F 25-205C (77-400F)
CTE, linear 500C14 m/m-C7.78 in/in-F 25-315C (77-600F)
CTE, linear 500C14.4 m/m-C8 in/in-F 25-425C (77-800F)
CTE, linear 1000C14.9 m/m-C8.28 in/in-F 25-540C (77-1000F)
CTE, linear 1000C15.5 m/m-C8.61 in/in-F 25-600C (77-1110F)
CTE, linear 1000C15.7 m/m-C8.72 in/in-F 25-700C (77-1290F)
CTE, linear 1000C16.6 m/m-C9.22 in/in-F 25-800C (77-1470F)
CTE, linear 1000C17.1 m/m-C9.5 in/in-F 25-900C (77-1650F)
Heat Capacity0.462 J/g-C0.11 BTU/lb-F RT
Heat Capacity at Elevated Temperature0.653 J/g-C0.156 BTU/lb-F 700C (1290F)
Heat Capacity at Elevated Temperature0.672 J/g-C0.161 BTU/lb-F 800C (1470F)
Heat Capacity at Elevated Temperature0.689 J/g-C0.165 BTU/lb-F 900C (1650F)
Heat Capacity at Elevated Temperature0.719 J/g-C0.172 BTU/lb-F 1100C (2010F)
Heat Capacity at Elevated Temperature0.732 J/g-C0.175 BTU/lb-F 1200C (2190F)
Heat Capacity at Elevated Temperature0.784 J/g-C0.187 BTU/lb-F 1000C (1830F)
Thermal Conductivity10.9 W/m-K75.6 BTU-in/hr-ft-F RT
Thermal Conductivity at Elevated Temperature21.8 W/m-K151 BTU-in/hr-ft-F 600C (1110F)
Thermal Conductivity at Elevated Temperature24.7 W/m-K171 BTU-in/hr-ft-F 700C (1290F)
Thermal Conductivity at Elevated Temperature26.1 W/m-K181 BTU-in/hr-ft-F 800C (1470F)
Thermal Conductivity at Elevated Temperature26.9 W/m-K187 BTU-in/hr-ft-F 900C (1650F)
Thermal Conductivity at Elevated Temperature28.7 W/m-K199 BTU-in/hr-ft-F 1000C (1830F)
Thermal Conductivity at Elevated Temperature31.1 W/m-K216 BTU-in/hr-ft-F 1100C (2010F)
Thermal Conductivity at Elevated Temperature32.9 W/m-K228 BTU-in/hr-ft-F 1200C (2190F)
Melting Point1293 - 1370 C2360 - 2500 F 
Solidus1293 C2360 F 
Liquidus1370 C2500 F 


This information is provided by MatWeb.com, The Online Materials Database and is reprinted with their permission.

Copyright 1996-2005 by Automation Creations, Inc. The contents, results, and technical data on this page may not be reproduced either electronically, photographically or substantively without permission from Automation Creations, Inc and MatWeb.com. No warranty, neither expressed nor implied, is given regarding the accuracy of this information. The user assumes all risk and liability in connection with the use of information from MatWeb.com.